Good Solderability Conductive Silver Paste 80% Silver Contain 30 - 65 Viscosity

Business Type
Manufacturer
Country
China
Category

Product Detail

Good Solderability 80% Silver Contain Conductive Silver Paste for Automotive Windshield





Description



DT5572(80% silver contain) is a well-developed conductive silver paste with high performance in printing hot wire for automotive backlights. This productdoes not contain toxic elements such as lead, in line with the EU ROHS Directive (2002/95/E).
Advantages of our conductive paste product: good printability & solderability, high adhesion & resistance stability.



Application



The silver paste is mainly applied on automobileelectrically heated glassfor defroster and/or defogger purposes.

It forms the pattern on the automobile glass through the silk screen printing process. After drying and heating process, the metal silver conductive wire is formed on the automobile glass. When the power is electrified, the heat can be generated and the frost on the glass can be removed.

The firing range is adapted to suit toughened glass requirements.



Specification





- - - -
Test | Properties |
DT5572 |
Ag Content (%) | 78-82 |
Viscosity (Pa.S) (NDJ-99,4#,10rpm,250.5) | 30-65 |
Fineness(m) | 15 |
Screen Mesh (Polyester mesh) | 200~280 |
Leveling Time | At room temperature, 2-3min |
Recommended Drying Conditions | 150-180/3min |
Recommended Firing Conditions | 600-650/3min |
Fired Thickness(m) | 12-15 |
Conductivity(m/sq) | 3 |
Drift of Resistance after Reliability Test (%) | 10 |
Adhesion((N) | 130 |
Shelf Life | Six Months from Date of Shipment |
- - - -



Featured Advantage



1.Wide firing temperature range
The firing temperature range is wide as 600-650 and it could meet most production process requirement.



2. Small change of resistance with long-time printing

The resistance drift could be controlled within 10% during lab testing. It shows the paste could keep stable performance after printing and firing process.



3. Good Acid Resistance

Put the sample soaked in 0.1N sulfuric acid solution(at room temperature) for at least 2 hours, remove the silver layer with adhesive tape and no Ag transfer, and the resistance drift is less than or equal to 8%.



4. Excellent anti-oxidation and anti-sulfide properties

Put the sample soaked in 400g ethanol plus 1g sulfur powder(elemental sulfur) solution for over 2 hours, the surface shall no significant change(yellow or black).





Why Choose Us?



1.Dedicated to high quality, stable supply and considerate service.



2.To inform customers of price trends in the market timely.



3.Provide considerate services to minimize clients worries.



4.Fast delivery: quick supply of sample in stock and 3-7 days for bulk production.



5.Customiszed production for different paste electrical properties requirements.

Similar Products

Electric Meter

Our Product Showcase

About our Company

Business Type
Manufacturer
Products
Electric Meter

Regional Suppliers

Electric Meter in China

Contact Us

Hunan LEED Electronic Ink Co., Ltd

Mr. LEED LEED

China

Send us a message