Polyamide hot melt adhesive and hemming adhesive DY-P404
- - - -
Acid Value,(mg KOH/g ) | 5 |
Amine Value,(mg KOH/g) | 3 |
Viscosity,(mpa.s/200C) | 10000-20000 |
Softening Point,(C) | 1205 |
Color,(Fe-Co ) | 8 |
Tensile Strength, ( MPa) | 20 |
Water absorption, ( %) | 0.4 |
Shear Strength, ( MPa, AL/AL) | 11 |
Stretch Rate, ( %) | 800 |
Peeling strength, ( N/25mm,PE/PE,602C) | 100 |
Operating Temperature( C ) | 160-200 |
- - - -
Yellowish round grain with schistose shape
This is a type of polyamide hot-melt adhesive with high performance, which is made from dimer acid and polyamine through condensation reaction at high temperature.
It can dissolve in general organic solvents, the hot-melting viscosity of the resin is greatly related to the temperature that it gets.
This polyamide hot-melt adhesive possesses the following advantages, such as lower viscosity, good fluidity, good flexibility, high adhesive strength, good media corrosion resistance, good solubility and fluxing property at low temperature, higher heat stability etc.
This type of resin is applied in heat-shrinkable sleeve for electric cable, sealing material for electrical connection, cementing or fixing materials for electronic component, bonding material for package, textile, leather, wood, plastic, metal and ceramics etc.
Packaging and Storage:
Double packing: craft paper-plastic composite bag lined with PE film.
Net weight: 25Kgs per bag.
Storage: kept in cool, airy and dry place, keep the package sealed before using up.
More appropriate price under the same quality as the one from our competitor.
Timely and effective service based on quality and technic.
Shorter lead time based on requirements from clients.